- 渗滤液浸泡对碱渣固化污泥长期性能的影响
- Influence of leachate soaking on long-term properties of sludge solidified with soda residue
- 何俊， 周莉蓉， 张磊， 冯潇莹
- 土木与环境工程学报 2023年45卷第3期 页码：164-172
- DOI：10.11835/j.issn.2096-6717.2021.134 中图分类号：X703.1
-
纸质出版日期：2023-06-25，
收稿日期：2021-03-06
-
引用本文
阅读全文PDF
扫 描 看 全 文
摘要
以碱渣—矿渣—生石灰固化污泥用作填埋场临时覆盖材料为背景，开展不同渗滤液浓度、浸泡时间和碱渣掺量条件下固化污泥性质的研究，探讨渗滤液浸泡对固化污泥长期性能的影响规律及微观机理。结果表明：固化污泥在渗滤液中长期浸泡时，生成钙钒石和水化硅酸钙等物质，试样强度随浸泡时间的增加而增大，固化污泥有较好的耐久性；但当碱渣掺量60%的试样浸泡210 d时，试样中生成大量的碳酸钙和不同尺寸的钙钒石，结构变得疏松，试样出现裂隙，强度大幅降低，低于垃圾填埋场临时覆盖材料强度要求，碱渣掺量过多对固化污泥的长期强度不利。渗滤液对固化污泥有一定的侵蚀性，固化污泥强度随渗滤液浓度的增大而降低。固化污泥具有结构性，不同渗滤液浓度和浸泡时间下固化污泥结构屈服应力变化与强度变化规律基本一致。在渗滤液长期浸泡过程中，碱渣—矿渣—生石灰对污泥和渗滤液中的铬、铜、铅、砷等污染物可起到稳定作用。
Abstract
Sewage sludge was solidified with soda residue (SR), ground granulated blast furnace slag (GGBS), and quicklime, which was used as a temporary covering material for landfills. The effect of leachate concentration, soaking time and SR content on the long-term properties of solidified sludge was carried out. The micro mechanism of long-term performance was investigated. The results indicate that hydration products such as ettringite and calcium silicate hydrate are generated when the solidified sludge is soaked in the leachate. The strength of the sample increases with the increase in soaking time, indicating that the solidified sludge has good durability to the leachate. Nevertheless, a large amount of calcium carbonate and ettringite of different sizes are generated in the sample with 60% SR content after being soaked for 210 d. Then the structure becomes loose, cracks appear in the sample, the strength decreases significanty, and its long-term strength reduces to lower than the strength requirement for temporary cover. Too much SR content is not good for the long-term strength of solidified sludge. The strength of solidified sludge decreases as the leachate concentration increases due to the corrosive effects of leachate. The solidified sludge is structural, and the changes in the yield stress under leachate soaking are basically similar to the strength. During the long-term leachate soaking, SR-GGBS-quicklime can stabilize some pollutions such as chromium, copper, lead and arsenic in the sludge and leachate.
参考文献
中华人民共和国住房和城乡建设部. 2019年城市建设统计年鉴[R/OL]. (2020-12-31) [2021-01-20]. http:// www.mohurd.gov.cn/xytj/tjzljsxytjgb/jstjnj/.[百度学术]
Ministry of Housing and Urban-Rural Development of the People’s Republic of China. Statistical Yearbook of Urban Construction in 2019 [R/OL]. (2020-12-31) [2021-01-20]. http:// www.mohurd.gov.cn/xytj/tjzljsxytjgb/jstjnj/.(in Chinese)[百度学术]
姜媛媛, 王彦, 段文焱, 等. 市政污泥热解过程中重金属迁移特性及环境效应评估[J]. 环境科学, 2021, 42(6): 2966-2974.[百度学术]
JIANG Y Y, WANG Y, DUAN W Y, et al. Migration and environmental effects of heavy metals in the pyrolysis of municipal sludge [J]. Environmental Science, 2021, 42(6): 2966-2974. (in Chinese)[百度学术]
VIEIRA R F, MORICONI W, PAZIANOTTO R A A. Residual and cumulative effects of soil application of sewage sludge on corn productivity [J]. Environmental Science and Pollution Research, 2014, 21(10): 6472-6481.[百度学术]
FAN X H, ZHU W, QIAN Y J, et al. Increasing the hydraulic conductivity of solidified sewage sludge for use as temporary landfill cover [J]. Advances in Civil Engineering, 2019, 2019: 1-10.[百度学术]
曹永华, 闫澍旺, 赵乐军. 固化污泥的工程性质及微观结构特征[J]. 岩土力学, 2006, 27(5): 740-744.[百度学术]
CAO Y H, YAN S W, ZHAO L J. Engineering properties and microstructure feature of solidified sludge [J]. Rock and Soil Mechanics, 2006, 27(5): 740-744. (in Chinese)[百度学术]
KIM E H, CHO J K, YIM S. Digested sewage sludge solidification by converter slag for landfill cover [J]. Chemosphere, 2005, 59(3): 387-395.[百度学术]
HERRMANN I, SVENSSON M, ECKE H, et al. Hydraulic conductivity of fly ash-sewage sludge mixes for use in landfill cover liners [J]. Water Research, 2009, 43(14): 3541-3547.[百度学术]
陈萍, 冯彬, 詹良通. 以垃圾焚烧底灰为骨料的脱水污泥固化试验[J]. 中国环境科学, 2014, 34(10): 2624-2630.[百度学术]
CHEN P, FENG B, ZHAN L T. Solidification of dewatered sewage sludge using bottom ash of MSWI as skeleton material [J]. China Environmental Science, 2014, 34(10): 2624-2630. (in Chinese)[百度学术]
ROSLI N A, AZIZ H A, SELAMAT M R, et al. A mixture of sewage sludge and red gypsum as an alternative material for temporary landfill cover [J]. Journal of Environmental Management, 2020, 263: 110420.[百度学术]
城镇污水处理厂污泥处置混合填埋用泥质: GB/T 23485—2009 [S]. 北京: 中国标准出版社, 2009.[百度学术]
Disposal of sludge from municipal wastewater treatment plant-Quality of sludge for co-landfiling: GB/T 23485—2009 [S]. Beijing: Standards Press of China, 2009 (in Chinese)[百度学术]
KJELDSEN P, BARLAZ M A, ROOKER A P, et al. Present and long-term composition of MSW landfill leachate: A review [J]. Critical Reviews in Environmental Science and Technology, 2002, 32(4): 297-336.[百度学术]
HE J, LI F, LI Y, et al. Modified sewage sludge as temporary landfill cover material [J]. Water Science and Engineering, 2015, 8(3): 257-262.[百度学术]
CHEN P, ZHAN L T, WILSON W. Experimental investigation on shear strength and permeability of a deeply dewatered sewage sludge for use in landfill covers [J]. Environmental Earth Sciences, 2014, 71(10): 4593-4602.[百度学术]
ZHANG H Y, YANG B, ZHANG G W, et al. Sewage sludge as barrier material for heavy metals in waste landfill [J]. Archives of Environmental Protection, 2016, 42(2): 52-58.[百度学术]
XU S C, LU H J, LIU J Z, et al. An experimental study on the microstructure and triaxial shear of structured clay in contact with landfill leachate [J]. Bulletin of Engineering Geology and the Environment, 2019, 78(6): 4611-4622.[百度学术]
李磊, 王佩, 薛飞. 生化降解条件下水泥固化污泥的微观结构研究[J]. 应用基础与工程科学学报, 2018, 26(6): 1217-1225.[百度学术]
LI L, WANG P, XUE F. Research on microstructure of solidified sludge using cement under biochemical degradation [J]. Journal of Basic Science and Engineering, 2018, 26(6): 1217-1225. (in Chinese)[百度学术]
孙家瑛, 顾昕. 新型无熟料碱渣固化土的工程特性[J]. 建筑材料学报, 2014, 17(6): 1031-1035.[百度学术]
SUN J Y, GU X. Engineering properties of the new non-clinker incorporating soda residue solidified soil [J]. Journal of Building Materials, 2014, 17(6): 1031-1035. (in Chinese)[百度学术]
HE J, LI Z X, WANG X Q, et al. Durability of soft soil treated with soda residue and ground granulated blast furnace slag in a soaking environment [J]. Journal of Materials in Civil Engineering, 2020, 32(3): 06019018.[百度学术]
刘晶晶, 查甫生, 王连斌, 等. 碱渣固化铅污染土淋滤特性试验研究[J]. 东南大学学报(自然科学版), 2016, 46(Sup1): 94-98.[百度学术]
LIU J J, ZHA F S, WANG L B, et al. Leaching properties of lead contaminated soils treated by soda residue [J]. Journal of Southeast University (Natural Science Edition), 2016, 46(Sup1): 94-98. (in Chinese)[百度学术]
栗志翔. 碱渣-矿渣固化市政污泥的工程性质试验研究[D]. 武汉: 湖北工业大学, 2020.[百度学术]
LI Z X. Experimental research on engineering properties of municipal sludge solidified with soda residue and ground granulated blast furnace slag [D]. Wuhan: Hubei University of Technology, 2020. (in Chinese)[百度学术]
公路土工试验规程： JTG 3430—2020 [S]. 北京： 人民交通出版社, 2020.[百度学术]
Test methods of soils for highway engineering: JTG 3430—2020 [S]. Beijing: China Communications Press, 2020. (in Chinese)[百度学术]
李磊, 徐菲, 周灵君, 等. 固化污泥压缩特性研究[J]. 岩土工程学报, 2015, 37(1): 171-176.[百度学术]
LI L, XU F, ZHOU L J, et al. Compression characteristics of solidified sewage sludge [J]. Chinese Journal of Geotechnical Engineering, 2015, 37(1): 171-176. (in Chinese)[百度学术]
XU J, LI Y F, REN C, et al. Damage of saline intact loess after dry-wet and its interpretation based on SEM and NMR [J]. Soils and Foundations, 2020, 60(4): 911-928.[百度学术]